Colloidal polypyrrole as binder for silicon anode in lithium ion batteries
Küçük Resim Yok
Tarih
2022
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Energy Storage
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
Silicon (Si)-based anodes have limited application in lithium ion batteries (LIBs) due to the loss of contact with current collector because of large volume change during lithiation and delithiation processes. In this study, pyrrole (Py) was polymerized chemically by cerium ammonium nitrate (CAN) and conductive colloidal polypyrrole (Col-PPy) was obtained in one step in N,N0 - dimethylformamide (DMF). To overcome problems during the volume change, Col-PPy was then used as polymeric binder with Si nanoparticle (SiNP) in Sianode and it called as “Col-PPy/SiNP.” In order to improve the cyclability and capacity of Si-anodes, Col-PPy solution was used also together with polyvinylidenefluoride (PVDF) and polyvinylpyrrolidone (PVP). These Si-anodes were further analyzed with cycle tests and combined cycle tests at different rates (C-rate) in half cells and scanning electron microscopy images of electrodes were taken before and after cycling. All results suggested that as an anode for LIB, Col-PPy/SiNP exhibited high reversible capacity (2617 mAh/g at C/10 [0.42 A/g]) and good cycling performance (reversible capacity of 1400 mAh/g after 189 cycles at C/3 [1.4 A/g]).
Açıklama
Anahtar Kelimeler
Colloidal polypyrrole, Lithium ion batteries, Silicon anode
Kaynak
Energy Storage
WoS Q Değeri
N/A
Scopus Q Değeri
Q3
Cilt
4
Sayı
4
Künye
Yayla, I.İ.A., Yuca, N., Sezer, E. and Ustamehmetoğlu, B. (2022). Colloidal polypyrrole as binder for silicon anode in lithium ion batteries. Energy Storage, 4(4).